DA Builders and Contractors

and non-ferrous metals such as aluminium, stainless steel, titanium FRP and even glass. It can be applied in harsh and adverse conditions for e.g., tidal zone areas, underwater applications and also to oily surfaces which gives simplicity of application to the applicator with minimum surface preparation. Versatile in which it can be applied onto wet or dry surfaces and displays excellent adhesion and compatibility to other coatings. Contains Zirconium and is suitable for rebuilding pitted surfaces up to 5mm. Solvent free system that is ideal for use for interior of drinking water tanks. The coating is suitable for use on the floor and interior for the food processing and manufacturing industry, Oil & Gas and power industry. Product Information
Colour Black, Grey, White and Yellow

Packing Size 10-kg and 20-kg pack

Non-Volatile Content 100%

Mixing Ratio Epoxy and Hardener (5:1) by Weight only

Full Cure 30°c in 48 Hours

Pot Life 30 to 40 mins at 30°c

Touch Dry 3 Hours with Walkover of 4 to 8 hours at 30°c

Temperature Resistance 5°c - 150°c

Chemical Resistance 75% H2SO4

Volume Solid 100%

Recommended DFT 100 - 200 µm

Coating Layer 1-2

Theoretical Coverage 10m2/litre (at DFT 100 µm ) * Allow for Application losses and Surface irregularities

Shelf Life At least 24 months when stored in sealed containers

Application Area
Tanks, Exterior of Steel and Iron Pipes

Coating onto GRE / Fiber Glass

Offshore structures, marine vessels, FPSO

Vessel linings under immersed conditions up to 150°C

Concrete Structures

Splash Zones, Tidal Zones, Flow Lines, Risers, Jetty's

Water Storage Tanks

Fishing Boats, Ships & Barges

Water Proofing

Gratings with minimum surface preparation

Bridges, Walkways, Bridge bearings, Railings

Decks, piping, storage tanks, ballast tanks

Acid Linings subject to type of acids

Concrete Repairs

Pressure Vessels, Storage Tanks, Turbine Ducts / Exhaust

Wooden Blocks, Glass, Stainless Steel Products

Industrial Floor Coatings

Roads (Zebra Crossing, Divider's etc..) Environmental

Blasting or application should NOT be carried out when:
Relative humidity is >95%

Substrate temperature below 4°C.